We have recently been discussing the best way to analyze the diffusion and SepCon separation gels. In the following figures, I present line scans of the gels. These appear to be a bit noisy and are somewhat misaligned due to…

Using wafer 302 I set up 2 20nm and 2 50nm gold diffusion experiments. After 24 hrs I removed the retentate and filtrate and looked for the gold using the Malvern Zetasizer. We can’t perform the diffusion with both 20nm…

My previous post outlined the results of a EQ format separations using membranes from wafer 319. I have followed up that experiment using the same membranes, but in a diffusion based separation. I separated 2uL of 9.3 mg/mL clarified brain…

We finally achieved a separation using the EQ format. 4 SepCons from wafer 319 were loaded with 500 uL of .93 mg/mL clarified brain extract. They were run at 1000 rpm (which we roughly figured to be 3.3 psi initially)…

Previously I had posted a chart depicting the permeabilities of SepCon membranes from w310. I went back and noticed some errors in the equations. Here is an updated version of that chart. Also included is a sample where I used…

Last week I performed spins with SepCons from w310. I tracked permeability and tried to perform some separations with proteins. w310 had high air permeability (link), but from my diffusion data it looked looked like the cutoff was possibly between…

This is some really preliminary data that I hope to add to in the next couple of days. Yesterday I prepared 4 SepCon samples from wafer 310. I spun them at 3.3 psi for 2 hours with just PBS. I…

This week I set up some diffusion experiments with the inner membranes of wafers 187 and 310. From the TEM images posted previously, we see that these inner membranes have what appear to be either very small pores or small…

Link to “A closer look at separations” We recently bought purified proteins that I will use to build a molecular weight ladder for membrane separations. I initially dissolved these proteins in salt solution and spun in an ultracentrifuge to remove…

We have previously discussed how the membranes near the center of the wafer have very small pores, while as you progress outward larger pores begin to appear. I tested one of these central membranes from wafer 304 (TEM sample, position…