Fibroblast adhesion experiment was done using poly-lysine coated plastic and teflon coverslips as positive and negative controls repectively. Poly-lysine is a polypeptide that gives the cells a sticky surface to adhere to. Teflon coverslips are used as negative control because…
Author: Anant Agrawal
Fibroblast Adhesion Update
Four more adhesion experiments were carried out and the results can be seen in the following charts. Based on the average of the four trials it can be elucidated that the initial adhesion (after ~7 hours) is pretty much the…
pH and Salt test on pncSi
We have been wondering about the reason for discoloration for a while. This could be due to the pH of the solution or the concentration of the salts in the solution. To narrow down our vision on this, first we…
HUVEC growth curve
HUVEC (P5) growth was monitored over 3 days on different substrates (glass coverslips, tissue culture treated & untreated plastic and RTPed pnc-Si from W510). The growth curve is as shown below and it can be observed that the growth rate…
HUVEC Growth and associated pnc-Si discoloration
HUVEC (P8) growth was monitored over 5 days on different substrates (glass coverslips, tissue culture treated plastic and pnc-Si from W510). The growth curve is as shown below and it can be observed that the growth rate on pncSi in…
HUVEC on pncSi
In order from left to right: 1) t=0, huvec on pncSi, in EGM (10% FBS) 2) t=24 hrs (cells reach confluence) 3) DIC after staining 4) FITC (live cells) 5) Rhodamine (dead cells) Its good to see the cells reach…
Posted in NRG
Update on RTP effect
From this updated post its evident that the O2 RTP treated samples start discoloring after ~10 days. Also, the O3 + O2 RTP treatment is probably better in preventing dicoloration than just O2 RTP. So amongst all the samples, the…
Posted in NRG
SiO2 coated membranes
The SiO2 coated samples (from W335 & W341) were found completely discolored after 5 days in DMEM (benchtop). Thus, silicon dioxide coating didn’t prevent discoloration as much as the RTP treatment. There’s a need to check the discoloration profile of…
Posted in NRG
Oxygen RTP better than Argon RTP
In continuation of the previous post, its been further observed that O2 RTP treated samples remain unchanged whereas the Ar RTP treated samples started to discolor after a week, as shown in the following images: In order (left to right)1.…
Posted in NRG