After all the nafion-coated pnc-Si chips that Jirachai gave me broke during my last attempt to filter salt water, Jirachai was kind enough to supply me with a new batch of chips, this one a mix of SiN and pnc-Si,…
Tag: SEM
SEM x-section of 30-50-30 NSN showing increased thickness after RTP
This is a continuation of earlier work showing 30-100-30 NSN x-sections where the Si layer thickness increases from ~92 nm before RTP to ~130 nm after RTP. Below are SEMs showing a ~50 nm thick a-Si film becoming a ~62 nm…
SEMs of burst 30-50-30 NSN SEPCON
Below are some SEM images of a burst 30-50-30 NSN membrane in a SEPCON pattern. Many similar chips failed at lower pressures, but this one survived to ~5-7 psi. (didn’t keep close track of the chips after they were burst,…
SEM Images of Barcikowski Samples
With Joe’s help, I was able to take some SEM images of the samples that I performed my previous set of separation experiments on. Sample 1: The obvious aggregation in this sample (exemplified by the ‘victory eagle’ blot in the…
Posted in NRG Tagged with: Barcikowski, clumping, dried sample, gold, karl, particles, platinum, SEM