Wafers 525 & 527 have a 1000 Å dry thermal oxide mask with all three films on the frontside sputtered. Both these wafers had a high density of pinholes. The pores are also irregular in shape and seem to have…

Last week’s production yielded two wafers (502 & 504) with defect-free membranes. 506 had a high pinhole density. These wafers have a TEOS mask and were annealed twice; the first anneals did not produce pores so they were annealed again…

I set out to do an in depth study of adsorption to various surfaces using the sample buffer method. Midway through staining the multiple gels I noticed there was a problem. It looked as though glass and polystyrene adsorbed about…

I recently tested the burst pressures of samples from W510, 511, and 513. None of the membranes are pinhole free. Silicon thickness varies (15 nm, 10 nm, 20 nm). See Dave’s post for complete fabrication information. W513 has noticeably higher…

In the previous adsorption trials I compared SepCons to MicroCons and NanoSeps. The SepCons appeared to have higher adsorption, which we thought may have been a result of the plastic used in the SepCon. I then removed membranes from MicroCons…

This is the protocol I use to measure band intensities. At the end of the explanation I will post and review my recent results concerning silver stain densitometry. First load a digitized gel into ImageJ Select Image>Type>8 bit to make…

I recently attempted a fibroblast (L1 3T3 cell line) growth test. The cells were seeded at too high of a density, so growth curves can’t be produced. However I checked cell viability and pnc-Si discoloration. As expected RTP treated samples…